- Model NO.: Dia 75-200mm Dia 30-300mm
- Type: General Rubber Machinery
- Type of Tire Machinery: Rubber Regeneration Machinery
- Nitrided Layer Depth: 0.5-0.8mm
- Nitrided Brittleness: Less Than Grade 1
- Linearity of Screw: 0.015mm
- Specification: ISO9001: 2008
- HS Code: 84779000
- Certification: ISO
- Type of General Rubber Machinery: Rubber Extruder
- Screw Barrel: Bimetallic Feed Screw and Barrel for Rubber
- Nitrided Hardness: 900-1000hv
- Surface Roughness: Ra0.4
- Trademark: Zhongyang
- Origin: Zhejiang of China
Specification:
Diameter of pin screw and barrel: Φ 75mm-Φ 200mm
Diameter of cold feed or hot feed screw and barrel: Φ 30mm-Φ 300 mm
L/D ratio: 12-18
Technical Information
Base Materials:
1)38CrMoAlA(JIS SACM645)
2)42CrMo(AISI 4140)
3)4Cr5MoSi V1 (JIS SKD-61)
4)9Cr18MOV
5)HPT
Bimetallic alloy materials:
1)Fe-based alloy
2)Ni-based alloy/Deloro alloy
3)Co-based alloy
4)NiCo-based alloy
5)Tungsten carbide/Wolfram carbide
Technics:
Heat treatment
High-frequency quenching
Nitriding treatment
Hard-chrome electroplating
Bimetallic alloy welding
Bimetallic alloy centrifugal casting
Technical parameter:
Nitrided layer depth: 0.5-0.8mm
Nitrided hardness: 900-1000HV
Nitrided brittleness: Less than grade 1
Surface roughness: Ra0.4
Linearity of screw: 0.015mm
Hard-chrome plating hardness after nitriding: >=950HV
Chrome-plating layer depth: 0.025-0.085mm
Bimetallic layer depth: 3mm
Warranty and service: 1 year
Our advantages:
1)Excellent raw materials
2)Good customer service
3)Rapid delivery
4)Reasonable price
5)Production quickly
Experienced manufacture, we will be the best choice.
Epoxy resin is a kind of polymer material with high performance. It is a two-component system composed of epoxy group and amine group, which forms polymer compound by mixing and reaction. It has strong adhesive force, corrosion resistance, heat resistance, electrical insulation and mechanical strength, and is widely used in aviation, aerospace, automotive, construction, electronics, ships and other fields.
The preparation process of epoxy resin is to mix epoxy resin monomer and amine Curing Agent in a certain proportion, and react at a certain temperature to form a polymer compound. Epoxy resins with different properties can be obtained by changing the type of monomer, the type and proportion of curing agent.
The advantage of epoxy resin is that its properties can be adjusted according to needs, and materials with high strength, high stiffness, high toughness, high temperature resistance, corrosion resistance and other characteristics can be prepared. Because of its excellent properties, epoxy resins are widely used in various fields. For example, in the aerospace field, epoxy resins are used in the manufacture of aircraft and rocket structural parts, composites, coatings and adhesives; In the automotive field, epoxy resins are used in the production of automobile body and engine parts; In the field of construction, epoxy resins are used in coatings, floors, waterproof materials and so on.
In addition, carbon fiber reinforced epoxy resin composites are also one of the most widely used epoxy resin products at present. Carbon fiber reinforced epoxy resin composites have the advantages of high strength, high modulus and low density, and are widely used in aviation, aerospace, automobile, sporting goods and other fields.
In general, epoxy resin is a high-performance material with a wide range of application prospects, and its properties can be adjusted according to needs, and it is widely used in various fields.
Epoxy Resins,Crystal Clear Epoxy Resin,Hardener Epoxy Resin,Liquid Epoxy Resin
Shanghai Shengduan Trading Co., Ltd. , https://www.sdcuringagent.com